API 5L Grade B ASTM A106 Carbon Seamless Steel Pipe 4 Inch SCH 40
Key Specifications / Features
Model No.: 1. HX- Carbon Steel Pipe -91 Hits: 103
China manufacturer of API 5L Grade B ASTM A106 Carbon Seamless Steel Pipe 4 Inch SCH 40
Request a quote
Share
Tags:
Detail Information
Standard: ASTM A106/A53
Steel Grades: Grade A ,Grade B, Grade C.
Size Range: OD:1/2” TO 24”. WT: 3mm To 45mm
Manufacturing Process : Hot Rolled / Hot Expansion/ Cold Drawn
Application:These pipes are used in the construction of boilers, piping systems and heating systems in chemical projects. A53 Pipes are intended for mechanical and pressure applications, as well as ordinary uses in steam,water, gas and airlines.
Packing: External Black Painting ,Both Side With End Caps, In Bundles by Steel Strips,Covered by Waterproof.
Steel Grades: Grade A ,Grade B, Grade C.
Size Range: OD:1/2” TO 24”. WT: 3mm To 45mm
Manufacturing Process : Hot Rolled / Hot Expansion/ Cold Drawn
Application:These pipes are used in the construction of boilers, piping systems and heating systems in chemical projects. A53 Pipes are intended for mechanical and pressure applications, as well as ordinary uses in steam,water, gas and airlines.
Packing: External Black Painting ,Both Side With End Caps, In Bundles by Steel Strips,Covered by Waterproof.
| ASTM A 106 Chemcial Composition | |||||||||||
| Stee grade |
Delivery condition |
C max |
Si max |
Mn max |
P max |
S max |
Ni max |
Cr max |
Cu max |
Mo max |
V max |
| A | Hot-finished | 0.25 | 0.10 | 0.27-0.93 | 0.035 | 0.035 | 0.400 | 0.400 | 0.400 | 0.150 | 0.080 |
| B | Hot-finished | 0.30 | 0.10 | 0.29-1.06 | 0.035 | 0.035 | 0.400 | 0.400 | 0.400 | 0.150 | 0.080 |
| C | Hot-finished | 0.30 | 0.10 | 0.29-1.06 | 0.035 | 0.035 | 0.400 | 0.400 | 0.400 | 0.150 | 0.080 |
| ASTM A 106 Mechanical Property | |||||||||||
| Steel grade | Yield strength Min (Mpa) |
Tensile strength Min(Mpa) |
Elongation A Min(%) |
||||||||
| A | 205 | 330 | AS PER ASME SA106/ASTM A106 |
||||||||
| B | 240 | 415 | |||||||||
| C | 275 | 485 | |||||||||